POM 107 美国杜邦公司 物性数据 |
规格级别: | 注塑级 | 外观颜色: | --- |
用途概述: | --- | ||
备注说明: | 特性:均聚甲醛,强度、刚度、热稳定性能好、硬度好。 |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
其它性能 | 弯曲降服强度 | +73?H | ASTM D-790 | 14.3 | MPsi |
基本性能 | 密度 | --- | ASTM D-792 | 1.42 | --- |
物理性能 | 吸水量 | 24hrs浸泡+73?H(+23℃) | ASTM D-570 | 0.25 | % |
吸水量 | Equil.50%R.h.+73?H(+23℃) | ASTM D-570 | 0.22 | % | |
吸水量 | 浸泡均衡点+73?H(+23℃) | ASTM D-570 | 0.90 | % | |
扩散因数 | +73?H(+23℃)106Hz | ASTM D-150 | 0.005 | --- | |
机械性能 | 洛氏硬度 | --- | ASTM D-785 | M94,R120 | --- |
摩擦系数 | +73?H(+23℃)静态 | ThrustWasherTest3 | 0.20 | --- | |
摩擦系数 | +73?H(+23℃)动态 | ThrustWasherTest3 | 0.35 | --- | |
挠曲系数 | +122℃ | 在25℃下 | 620 | MPa | |
弯曲降服强度 | +23℃ | ASTM D-790 | 98.6 | MPa | |
压缩应力 | +73?H@1%Def. | ASTM D-695 | 5.2 | MPsi | |
挠曲系数 | +70℃ | 在25℃下 | 1550 | MPa | |
挠曲系数 | +212?H | 在25℃下 | 130 | MPsi | |
挠曲系数 | +100℃ | 25℃下 | 895 | MPa | |
挠曲系数 | +250?H | 在25℃下 | 90 | MPsi | |
弹性系数 | +23℃ | ASTM D-638 | 3100 | MPa | |
剪力 | +73?H | ASTM D-732 | 9.5 | MPsi | |
剪力 | +23℃ | ASTM D-732 | 65.5 | MPa | |
挠曲系数 | -68?H | 在25℃下 | 530 | MPsi | |
挠曲系数 | -55℃ | 在25℃下 | 3650 | MPa | |
挠曲系数 | +73?H | 在25℃下 | 380 | MPsi | |
挠曲系数 | +23℃ | 在25℃下 | 2620 | MPa | |
挠曲系数 | +158?H | 在25℃下 | 225 | MPsi | |
断裂时之拉力伸张度 | -68?H(-55℃) | ASTM D-638 | 38 | % | |
断裂时之拉力伸张度 | +73?H(+23℃) | ASTM D-638 | 75 | % | |
断裂时之拉力伸张度 | +158?H(+70℃) | ASTM D-638 | 230 | % | |
断裂时之拉力伸张度 | +212?H(+100℃) | ASTM D-638 | >260 | % | |
断裂时之拉力伸张度 | +250?H(+122℃) | ASTM D-638 | >260 | % | |
伸张强度 | -68?H | ASTM D-638 | 14.7 | MPsi | |
伸张强度 | -55℃ | ASTM D-638 | 101 | MPa | |
伸张强度 | +73?H | ASTM D-638 | 10.0 | MPsi | |
伸张强度 | +23℃ | ASTM D-638 | 68.9 | MPa | |
伸张强度 | +158?H | ASTM D-638 | 6.9 | MPsi | |
伸张强度 | +70℃ | ASTM D-638 | 6.9 | MPa | |
伸张强度 | +212?H | ASTM D-638 | 5.2 | MPsi | |
伸张强度 | +250?H | ASTM D-638 | 3.8 | MPsi | |
伸张强度 | +122℃ | ASTM D-638 | 26.2 | MPa | |
伸张强度 | +100℃ | ASTM D-638 | 35.9 | MPa | |
弹性系数 | +73?H | ASTM D-638 | 450 | MPsi | |
压缩应力 | +23℃@1%Def. | ASTM D-695 | 35.9 | MPa | |
压缩应力 | +73?H@10%Def | ASTM D-695 | 18.0 | MPsi | |
压缩应力 | +23℃@10%Def. | ASTM D-695 | 124 | MPa | |
负载下之变形 | 2000psi@+122?H(14Mpa@50℃) | ASTM D-621 | 0.5 | % | |
弯曲疲劳忍耐限度 | +73?H | ASTM D-671 | 4.7 | MPsi | |
弯曲疲劳忍耐限度 | +23℃ | ASTM D-671 | 32.4 | MPa | |
IZOD冲击强度 | -40?H | ASTM D-256 | 1.8 | ft.lb/in | |
IZOD冲击强度 | 40℃ | ASTM D-256 | 96. |